The Study of Reactions Mechanism, Microstructure and Mechanical Properties of In Situ Composite Produced In Al-V2O5 System

Document Type : Original Articles

Authors

Mohammad Ashnagar ¹

Alireza Mashreghi ²

Mehdi Kalantar ²

¹ Mining and metallurgy, Yazd University, Yazd

² Yazd University

10.22067/ma.v27i1.24570

Abstract

In this research, fabrication of an in-situ composite via aluminothermic combustion synthesis in Al–V2O5 system has been investigated. For this purpose, the mixed powders of Al and V2O5 with molar ratio of 28 to 3 were ball milled and then compressed. Differential thermal analysis was used to evaluate the temperatures of phase transitions. Using the peak temperature of the reactions, the samples were subjected to heat treatment. It was shown that the reduction reaction of V2O5 by Al is a stepwise process and V2O4 and V2O3 as the main intermediate phases and γ-Al2O3 and Al23V4 as the transmission phases were formed before the formation of Al3V and α- Al2O3. Microstructural studies showed that after sintering at the temperatures up to 1000 ºC, Al8V5 phase is formed at the interface between the two phases of Al3V and α-Al2O3. Hardness and compression test results also showed that the hardness and strength of the samples increase with increasing heating temperature due to the formation of greater volume fraction of intermetallic compounds and ceramic phases, however, the compressive strain decreased because of the formation of a greater amount of the brittle phase Al8V5.

Keywords

in situ composite

Intermetallic compounds

aluminothermic

Differential thermal analysis

---

References

1. Chawla, K., "Composite Materials Science and Engineering", 4th Edition, Dep. of Materials and Metallurgical Engineering, New Mexico Socorro, pp. 4-24, (1989).
2. Schaffer, G.B., Hall, B. J, "The Influence of the Atmosphere on the Sintering of Aluminum", Metallurgical and Materials Transactions, Vol. 33, 3279-3284, (2002).
3. Zhong-Chun, C., Takenobu, T., Keisuke, I., "Microstructural evolution of reactive-sintered aluminum matrix composites", Composites Science and Technology, Vol. 68, pp. 2245–2253,(2008).
4. Travitzky, N., Gotman, I., Claussen, N., "Alumina–Ti Aluminide interpenetrating composites microstructure and mechanical properties", Materials Letters, Vol. 57, pp.3422– 3426,(2003).
5. Ai, T.T., "Microstructure and mechanical properties of in-situ Al2O3/TiAl composites by exothermic dispersion method", Acta Metall. Sin. (Engl. Lett.), Vol. 21, pp.437-443, (2008).
6. Yazdian, N., Karimzadeh, F., Enayati, M.H., "In-situ fabrication of Al3V/Al2O3 nanocomposite through mechanochemical synthesis and evaluation of its mechanism", Advanced Powder Technology, Vol. 24, pp. 106-112, (2013).
7. Woo, K., Kim, J., Kwon, E., "Fabrication of Al Matrix Composite Reinforced with Submicrometer- Sized Al2O3Particles Formed by Combustion Reaction between HEMM Al and V2O5 Composite Particles during Sintering", Met. Mater. Int, Vol. 16, pp. 213-218, (2010).
8. Huber, B., "Phase Diagram Investigations in the Ternary Systems Al-Co-Si and Al-Si-V ", Ph.D. Thesis, Vienna university, Germany, pp. 26-27, (2010).
9. Yang, H., McCormic, P.G., "Mechanochemical Reduction Of V2O5", journal of solid state chemistry, Vol. 110, pp. 136-141, (1994).
10. Travitzky, N., Gotman, I., Claussen, N., "Alumina–Ti Aluminide interpenetrating composites; microstructure and mechanical properties", Materials Letters, Vol. 57, pp. 3422–3426, (2003).
11. Shengzhong, K., Guangji, X., Yutian,D., "Effect of high-energy Ball Milling on Synthetic Reaction in Al- TiO2- C System", Journal of Wuhan University of Technology, Vol. 20, pp. 50-54, (2005).
12. Zhu, H., Min, M., Li,J., Ai, J., Ge, L., Wang, H., "In situ fabrication of (α-Al2O3 + Al3Zr)/Al composites in an Al–ZrO2 system", Composites Science and Technology, Vol. 70,pp.2183–2189, (2010).
13. Zhu, H., Jar, J., Song, J., Zhao, J., Li, J., Xie, Z., "High temperature dry sliding friction and wear behavior of aluminum matrix composites (Al3Zr-α-Al2O3)/Al", Tribology International, Vol. 48, pp. 78–86, (2012).
14. Zhu, H., Yao, Y., Li, J., Chen, SH., Zhao, J, Wang, H., "Study on the reaction mechanism and mechanical properties of aluminum matrix composites fabricated in an Al–ZrO2–B system", Materials Chemistry and Physics, Vol. 127,pp. 179–184, (2011).
15. Zhu, H., Min, J., Li, J., Chen, J., Zhao, J., Yao, Y., "Influence of B/ZrO2 molar ratios on the ambient temperature wear properties of composites made by an Al–ZrO2–B system", Wear, Vol. 271,pp. 635– 639, (2011).
16. Zhu, H., Min, J., Ai, Y., Chu, D., Wang, H., "The reaction mechanism and mechanical properties of the composites fabricated in an Al–ZrO2–C system", Materials Science and Engineering A, Vol. 527, pp. 6178–6183, (2010).
17. Zhu, H., Ai, Y, Min, J., Wu, Q., Wang, H., "Dry sliding wear behavior of Al-based composites fabricated by exothermic dispersion reaction in an Al–ZrO2–C system", Wear, Vol. 268, pp.1465–1471, (2010).
18. Zhang, D. L., Adam, G., Langdon, A. G., "Phase and microstructural evolution during heating of mechanically milled Al/V2O5 composite powders", Materials Science and Technology, Vol. 18, pp 901-907, (2002).
19. http://www.crct.polymtl.ca/factsage/fs_reaction.php