The Effect of Annealing on the Hardness and Microstructural Characterization of TM-321 Superalloy

Document Type : Original Article

Authors

abolfazl rastegaran

Masumeh Seifollahi

adly Akhond Zadeh

Faculty of Materials and Manufacturing Technologies, Malek Ashtar University of Technology, Iran.

10.22067/jmme.2025.87922.1148

Abstract

In this research, the effects of solution annealing heat treatment on the hardness and microstructure characteristic of TM-321 Ni base superalloy are investigated. The temperature of annealing was chosen on the basis of thermodynamic analysis of Procast 2018 for TM-321 superalloy. At 1080°C the volume percent of γ/γ′ eutectic pool which was 9 Vol% in the as cast structure reduced to 1.7 vol% at 4h and it is stable till 6h. At 1180°C again it is considerably decreased to 1.2 vol%. At 1180°C and times more than 2h, numerous and fine clusters of γ′ precipitates formed. The formation of γ′ precipitates clusters will disrupt the creation of the proper distribution of γ′ precipitates. At 1180°C/2h, the lowest eutectic volume fraction (0.9%), the highest dissolution and reduction in the fraction and size of primary γ′ (21.5% and 84nm) are present, which has been chosen as the best conditions for solutionizing in this research.

Keywords

TM-321 superalloy

solution annealing

γ/γ′ eutectic

γ′ precipitate

Subjects

• Physical Metallurgy

---

References

[1] H. Harada and, N. Rene, “High temperature materials for gas turbines : the present and future,” Proccceding International Gas Turbine Congress, pp. 1-9. 2003.

[2] K. H. M.Yamazaki, “JapanPatent #JP59059854A2,” Japan Science and Technology Agency, 1982.

[3] M. Yoritaka, Y. Yamamoto, Y. Hasegawa, and T. Hokari, “Automotive Application of Advanced Superalloys,” Journal of Materials, vol. 38, no. 12, pp. 20-22, 1986.

[4] J. R. Kattus, MAR M 247-Aerospace Structural Metals Handbook. West Lafayette: Purdue Research Foundation, 1999.

[5] H. T. Lee, and S. W. Lee, “The Morphology and Formation of Gamma Prime in Nickel-Base Superalloy,” Journal of Materials Science Letter, vol. 9, pp. 516-517, 1990.

[6] I. M. Wolff, “Precipitation Accompanying Overheating in Nickel-Base Superalloy,” Materials Performance, vol. 29, pp. 516-517, 1992.

[7] M. Mostafaei, and S. M. Abbasi, “Solutioning and solidification process control in Ta-modified CM247 LC superalloy,” Journal of Materials Processing and Technology, vol. 231, pp. 113-124, 2016.

[8]  G. Zhao, X. Zang, S. Gao, “Effect of Zr on As-cast and As-homogenized Microstructures of High Al+Ti Containing Ni-Based Superalloy,” Rare Metal Materials and Engineering, vol. 51, no. 9, pp. 3372-3380, 2023.

[9] Y. L. Tsai, S. F. Wang, H. Y. Bor, and Y. F. Hsu, “Effects of alloy elements on microstructure and creep properties of fine-grained nickel-based superalloys at moderate temperatures,” Materials Science and Engineering A, vol. 571, pp. 155-160, 2013.

[10] Y. L. Tsai, S. F. Wang, H. Y. Bor, and Y. F. Hsu, “Effects of Zr addition on the microstructure and mechanical behavior of a fine-grained nickel-based superalloy at elevated temperatures,” Materials Science and Engineering: A, vol. 607, pp. 294-301, 2014.

[11] Q. Z. Chen, C. N. Jones, and D. M. Knowles, “The grain boundary microstructures of the base and modified RR 2072 bicrystal superalloys and their effects on the creep properties,” Materials Science and Engineering: A, vol. 385, pp. 402-418, 2004.

[12] F. Theska, W. F. Tse, M. Schulz, M. Lison-Pick, S. Primig, “Review of Microstructure–Mechanical Property Relationships in Cast and Wrought Ni-Based Superalloys with Boron, Carbon, and Zirconium Microalloying Additions,” Advanced Engineering Materials, vol. 25, no. 8, pp.2201514, 2023.

[13] Y. Zhou, Y. Cui, B. Wang, S. Li, J. Wang, “Effects of Zirconium Additions on the Microstructure and Stress-Rupture Properties in Polycrystalline Ni-Based Superalloys,” Minerals, Metals and Materials Series, pp. 166-175, 2024.

[14] M. R. Barajas Álvarez, A. Bedolla Jacuinde, V.H. López Morelos, A. Medina Flores, A. Ruiz, “Improving the High-Temperature Creep Resistance of a Cast Co-Cr-W-Ni Superalloy with Additions of B and Zr,” Journal of Materials Engineering and Performance, vol. 33, no. 17, pp. 9226-9243, 2024.

[15] B. Kang, Y. Lee, J. Kim, T. Ha, Y. Kim, “Microstructural Analysis on Grain Boundary of Boron– and Zirconium–Containing Wrought Nickel-Based Superalloys,” Crystals, vol. 14, no. 3, pp. 290-295, 2024.

[16] M. J. Donachie, and S.J. Donachie, Superalloys a Technical Guide, 2nd ed. ASM International, 2002.

[17] M. Rahimian, “Physical simulation of investment casting of Mar-M247 Ni-based sueralloy,”phd thesis, Carlos III University of Madrid, 2015.

[18] H. Bor, C. Wei, A. Yeh, W. He, H. Wang and C. Kuo, “Heat treatment effects on the high temperature mechanical behavior of directionally solidified mar-m 247 superalloy,” Proceedings of the 8^th Pacific Rim International Congress on Advanced Materiala and Processing, springer, 2013, pp. 379-386.

[19] R. Baldan, R. L. P. Rocha, R. B. Tomasiello and C. A. Nunes,“Solutioning and Aging of MAR-M247 Nickel-Based Superalloy,” Journal of Materials Engineering and Performance, vol. 22, no. 9, pp. 2574-2579, 2013.

[20] O. Kubaschewski, “Thermodynamics of Solids,” International Metallurgical Reviews, vol. 18, no.2, pp. 89-90, 1973.

[21] F.C. Campbell, Fatigue and fracture, understanding the Basics. Ohio: ASM International, 2012.

[22] J. Zyka, I. Andrsova, J. Malek, B. Podhorna, A. Joch and K. Hrbacek, “Microstructure and mechanical properties of MAR-M-247 nickel superalloy,” 5th Anniversary International Conference on Metallurgy and Materials, Conference Proceedings, pp. 1606-1611, 2016.

[23] Y. Haruna, “Removal of Inclusions from cast superalloy Revert,”, Sanyo Technical Report, vol. 2, pp. 41-49, 1995.

[24] X. Dong, X. Zhang, K. Du, Y. Zhou, T. Jin, and H. Ye, “Microstructure of Carbides at Grain Boundaries in Nickel Based Superalloys,” Journal of Material Science and Technology, vol. 28, pp. 1031-1038, 2012.

 [25]  H.T. Kim, S. S. Chun, X. Yao, Y. Fang, J. Choi, “Gamma prime precipitating and ageing behaviours in two newly developed nickel-base superalloys,” Journal of Material Science, vol. 32, pp. 4917-4923, 1997.