In this research, the effects of temperature, time and grinding on the types of phases in the calcined kaolin and calcite mixture was investigated. Differential thermal analysis (DTA) and X-Ray diffraction of samples showed that gehlenite is formed at 990 ˚C as the main phase which transforms into anorthite with an increase in the temperature to 1200 ˚C. After grinding the mixture and with increasing the grinding time at the calcination temperature of 900 ˚C, anorthite was recognized to be the main phase.
saghian, M., naghizade, R., & sarpolaki, H. (2014). An Investigation into the Phase Formation during Calcination of Kaolin and Calcite Mixture. Journal Of Metallurgical and Materials Engineering, 25(1), -. doi: 10.22067/ma.v25i1.35739
MLA
mohamad saghian; rahim naghizade; hosin sarpolaki. "An Investigation into the Phase Formation during Calcination of Kaolin and Calcite Mixture". Journal Of Metallurgical and Materials Engineering, 25, 1, 2014, -. doi: 10.22067/ma.v25i1.35739
HARVARD
saghian, M., naghizade, R., sarpolaki, H. (2014). 'An Investigation into the Phase Formation during Calcination of Kaolin and Calcite Mixture', Journal Of Metallurgical and Materials Engineering, 25(1), pp. -. doi: 10.22067/ma.v25i1.35739
VANCOUVER
saghian, M., naghizade, R., sarpolaki, H. An Investigation into the Phase Formation during Calcination of Kaolin and Calcite Mixture. Journal Of Metallurgical and Materials Engineering, 2014; 25(1): -. doi: 10.22067/ma.v25i1.35739
)
Send comment about this article