Effect of Electrodeposition Parameters on Chemical Composition, Cathodic Current Efficiency, Hardness and Morphology of Zn-Ni Alloy Coatings

Document Type : Original Articles

Authors

• Mahshid Tafreshi ¹
• Saeed Reza Allahkaram ²
• Hassan Farhangi ³

¹ Islamic Azad University South Tehran Branch

² College of Engineering, University of Tehran

³ University of Tehran

10.22067/ma.v0i29.47786

Abstract

Zn–Ni alloy coatings were electrodeposited from acidic sulphate baths. In this study, the effect of plating parameters and bath composition on the cathodic current efficiency, as well as hardness, morphology and chemical composition of the coatings were investigated. The morphology and chemical composition of the coatings were investigated using scanning electron microscopy equipped with EDAX analyzer. Results showed that surface morphology and chemical composition of the films were strongly dependent on the electrodeposition parameters. Ni content and hardness of the coatings were increased and the cathodic current efficiency was decreased by enhancing the bath temperature and Zn (II)/Ni (II) ratios, or reducing the current density and bath pH. Electron microscopy images showed that cracks appeared on the coatings surface with increasing temperature due to the high residual stress. In addition, the structure of the coatings became finer with increasing the current density, resulting in the formation of voids and porosities. Studies on the bath pH revealed that only the coatings which were deposited in baths with pH=2 had a dense and uniform surface. Moreover, increasing the Zn (II)/Ni (II) ratios in the bath caused brittleness of the coatings.

Keywords

• Zn-Ni Alloy Coating
• chemical composition
• morphology
• Cathodic Current Efficiency
• Hydrogen Evolution

---

References

1. Marder A., "The metallurgy of zinc-coated steel", Progress in materials science, Vol. 45, pp. 191-271, (2000).
2. Boshkov N., "Influence of the alloying component on the protective ability of some zinc galvanic coatings", Electrochimica Acta, Vol. 51, pp. 77-84, (2005).
3. Crotty D., "Zinc alloy plating for the automotive industry", Metal Finishing, Vol. 94, pp. 54-58, (1996).
4. Sorkhabi H.A., Hagrah A., Ahmadi N.P., Manzoori J., ”Zinc-nickel alloy coatings electrodeposited from a chloridebath using direct and pulse current”, Surface and Coatings Technology, Vol. 140, pp. 278-283, (2001).
5. Conde A., Arenas M.A., de Damborenea J.J., "Electrodeposition of Zn–Ni coatings as Cd replacement for corrosion protection of high strength steel", Corrosion Science, Vol. 53, pp. 1489–1497, (2011).
6. Wilcox G.D., Gabe D.R., "Electrodeposited zinc alloy coatings", Corrosion Science, Vol. 35, pp. 1251–1258, (1993).
7. Brenner A., "Electrodeposition of Alloys, Principles and Practice", Chap. 1, Academic Press, New York, (1963).
8. Ghaziof S., Gao W., "Electrodeposition of single gamma phased Zn–Ni alloy coatings from additive-free acidic bath", Applied Surface Science, Vol. 311, pp. 635–642, (2014).
9. Lee H.Y., Kim S.G., "Characteristic of Ni deposition in an alkaline bath for Zn-Ni depositional steel plates", Surface and Coating Technology, Vol. 135, pp. 69-74, (2000).
10. Qiao X., Li H., Zhao W., Li D., "Effects of deposition temperature on electrodeposition of zinc-nickle alloy coatings", Electrochimica Acta, Vol. 89, pp. 771– 77, (2013).
11. مهرجوئی م.، مدرس ح.، سرابی ع. ،"بررسی برخی از خواص فیزیکی و شیمیایی آلیاژی Zn- Ni ایجاد سده در حمام‌های اسیدی"، علوم پایه و مهندسی کاربردی، ج. 56، صفحه 1220-1229، (1383).
12. Alfantazi A.M., Erb U., "Pulse-Plated Zinc-Nickel Alloy Coatings", Corrosion Engineering, Vol. 52, pp. 880-888, )1996).
13. Nakano H., Arakawa S., Takada Y., Oue S., Kobayashi S., "Electrodeposition Behavior of a Zn-Ni Alloy in an Alkaline Zincate Solution", Materials Transactions, Vol. 53, No. 11, pp. 1946-1951, (2012).
14. Muller C., Saret M., Benballa M., "Complexing agent for a Zn-Ni alkaline bath", Journal of Electroanalytical Chemistry, Vol. 519, pp. 85-92, (2002).
15. Lehman E.B., Ozgaa P., Swiatek Z., Lupi C., "Electrodeposition of Zn–Ni protective coatings fromsulfate –acetate baths", Surface and Coatings Technology, Vol. 151 –152, pp. 444–448, (2002).
16. Tian L., Xu J., Xiao S., "The influence of pH and bath composition on the properties of Ni–Co coatings synthesized by electrodeposition", Vacuum, Vol. 86, pp. 27-33, (2011).
17. Abdelrehim S.S., Fouad E.E., Abdelwahab S.M., "Electroplating of zinc–nickel binary alloys from acetate baths", Electrochimica Acta, Vol. 41, pp. 1413, (1996).
18. پولادی س. ، شریعت م.ح.، بحرالعلوم م.، "لایه نشانی آلیاژ Ni-Zn-P و نانو کامپوزیت Ni-Zn-P/nano SiC از یک حمام جدید به روش آبکاری الکتریکی و برررسی ویژگی‌های خوردگی آن"، مجله‌ی مواد نوین، جلد 2، شماره‌ 2، صفحه 72، (1390).